| Line 32: | Line 32: | ||
* shrinkage expansion after solidification: Clow136 skrinks 2x10-4. For a thickness of 2mm, that is less than 1 micron, so probably irrelvant. For Field's metal, we don't know. | * shrinkage expansion after solidification: Clow136 skrinks 2x10-4. For a thickness of 2mm, that is less than 1 micron, so probably irrelvant. For Field's metal, we don't know. | ||
| − | * | + | * expansion coefficient? Both should be very close to Al (22-23x10^-6/�C). |
| − | * | + | * melting temperature/conductivity? (how warm could foil become while machining?) |
| − | * | + | * fluidity: how easily does it flow? does it have sufficient capillary action to make a good film between foil and mold? |
| − | * Al affinity: | + | * Al affinity: does it stick well to the Al during milling in its solid phase? can we easily get it off again in its liquid phase? |
* recoverability: stuff is rather expensive (count 5 liter for final box?). how well can we recover it? | * recoverability: stuff is rather expensive (count 5 liter for final box?). how well can we recover it? | ||
| + | * toxity: Field's metal does not contain lead and less bismuth | ||